Development of technology for obtaining anticorrosion coatings on gas pipelines

This study is aimed at developing a bitumen-alkyd anticorrosion coating for steel gas pipelines using locally available raw materials.BND 60/90 bitumen, PF-060 alkyd varnish, hydrocarbon liquids, microcalcite, and zinc oxide were used to prepare five coating formulations.The effect of formulation composition on bitumen dissolution, drying behavior, adhesion, water uptake, and corrosion resistance was evaluated.Pyrolysis distillate showed the highest bitumen dissolution at 25-45 °C and was selected as the preferred processing liquid.Among the tested compositions, F5, containing 25 wt.% bitumen, 30 wt.% alkyd varnish, 30 wt.% pyrolysis distillate, 10 wt.% microcalcite, and 5 wt.%ZnO, showed the shortest drying time and the highest reported adhesion index.Salt-spray and NaCl exposure tests indicated delayed visible corrosion of coated steel compared with uncoated specimens.The obtained results confirm the practical potential of the developed coating for further pipeline protection studies.влияние состава на растворимость битума, скорость высыхания, адгезию, водопоглощение и коррозионную стойкость.Пиролизный дистиллят обеспечил наилучшую растворимость битума в диапазоне температур 25-45 °C и был выбран в качестве предпочтительного растворителя.Среди испытанных составов вариант F5, содержащий 25 мас.% битума, 30 мас. % алкидного лака, 30 мас. % пиролизного дистиллята, 10 мас.% микрокальцита и 5 мас.% ZnO, продемонстрировал наименьшее время высыхания и наиболее высокий показатель адгезии.Испытания в камере соляного тумана и в среде NaCl показали, что появление видимых признаков коррозии на стали с покрытием задерживается по сравнению с образцами без покрытия.Полученные результаты подтверждают практический потенциал разработанного покрытия для дальнейших исследований в области защиты трубопроводов.