Corrosion Behavior of Cu-7Ni-3Al-1Fe-1Mn Alloy Subjected to Different Processing Techniques

Copper–nickel alloys are critical materials for marine engineering, and their corrosion resistance is closely related to their microstructural states. However, the mechanism by which processing technologies regulate corrosion behavior through altering grain boundary character distribution remains unclear. In this study, the corrosion behavior of a Cu–7Ni–3Al–1Fe–1Mn alloy in 3.50 wt% NaCl solution was compared among three states: as-cast (AC), 60% deformation orthogonally cross-rolled (CR), and hot-extruded (HE) with an extrusion ratio of 12.30. The aim was to reveal the key role of grain boundary character distribution in corrosion behavior. The results showed that the corrosion resistance order was HE > CR > AC, with corrosion rates of 0.0062, 0.0068, and 0.015 mm/a, respectively. CR exhibited sufficient recrystallization (83.80%) and was dominated by high-angle grain boundaries, resulting in continuous intergranular corrosion. HE showed a low degree of recrystallization (25%), but possessed high absolute densities of CSL grain boundaries and triple junctions; its corrosion behavior was dominated by uniform dissolution and shallow pitting, with intergranular corrosion suppressed. The key factor determining the resistance to intergranular corrosion was the absolute number (density per unit area) of coincidence site lattice (CSL) grain boundaries rather than their relative proportion. Processing technologies regulate grain boundary character distribution and thereby alter corrosion paths: interconnected high-angle grain boundary networks lead to intergranular corrosion, whereas dense CSL grain boundary networks lead to uniform dissolution. Hot extrusion achieved both grain refinement and optimization of the CSL grain boundary network, transforming the corrosion mode from destructive localized corrosion to uniform and safe corrosion. These findings provide theoretical support for grain boundary engineering design of copper–nickel alloys for marine engineering.

Authors

Institutions

Publication Details

Published
2026-10-30
DOI
https://doi.org/10.66729/jhpap202608013
Primary Topic
Metallurgy and Material Science
Type
article
Field-Weighted Citation Impact
0.00
Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Corrosion Behavior of Cu-7Ni-3Al-1Fe-1Mn Alloy Subjected to Different Processing Techniques

Haitao Liu, Kexing Song, Lanqing Niu
2 links
Metallurgy and Material Science
article

Corrosion Behavior of Cu-7Ni-3Al-1Fe-1Mn Alloy Subjected to Different Processing Techniques

Haitao Liu, Kexing Song, Lanqing Niu
article en

Abstract

Copper–nickel alloys are critical materials for marine engineering, and their corrosion resistance is closely related to their microstructural states. However, the mechanism by which processing technologies regulate corrosion behavior through altering grain boundary character distribution remains unclear. In this study, the corrosion behavior of a Cu–7Ni–3Al–1Fe–1Mn alloy in 3.50 wt% NaCl solution was compared among three states: as-cast (AC), 60% deformation orthogonally cross-rolled (CR), and hot-extruded (HE) with an extrusion ratio of 12.30. The aim was to reveal the key role of grain boundary character distribution in corrosion behavior. The results showed that the corrosion resistance order was HE > CR > AC, with corrosion rates of 0.0062, 0.0068, and 0.015 mm/a, respectively. CR exhibited sufficient recrystallization (83.80%) and was dominated by high-angle grain boundaries, resulting in continuous intergranular corrosion. HE showed a low degree of recrystallization (25%), but possessed high absolute densities of CSL grain boundaries and triple junctions; its corrosion behavior was dominated by uniform dissolution and shallow pitting, with intergranular corrosion suppressed. The key factor determining the resistance to intergranular corrosion was the absolute number (density per unit area) of coincidence site lattice (CSL) grain boundaries rather than their relative proportion. Processing technologies regulate grain boundary character distribution and thereby alter corrosion paths: interconnected high-angle grain boundary networks lead to intergranular corrosion, whereas dense CSL grain boundary networks lead to uniform dissolution. Hot extrusion achieved both grain refinement and optimization of the CSL grain boundary network, transforming the corrosion mode from destructive localized corrosion to uniform and safe corrosion. These findings provide theoretical support for grain boundary engineering design of copper–nickel alloys for marine engineering.

Vol. 1(1)
Henan University of Science and Technology (CN), Henan Academy of Sciences (CN)
Openalex Percentile: Top 29%
Metallurgy and Material Science
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.

Laika access coming soon
Corrosion Behavior of Cu-7Ni-3Al-1Fe-1Mn Alloy Subjected to Different Processing Techniques — Haitao Liu, Kexing Song, et al. · (2026) | TGRS Research Map | TGRS