Correlation between real sieving coefficient determined using novel lab-scale module and pore structure of hemodiafiltration membranes

Abstract The novel lab-scale hollow fiber membrane module was fabricated to determine the apparent sieving coefficient ( $${SC}_{obs}$$ ) of commercial hemodiafiltration membranes, MFX-SW eco (polyethersulfone, Sample A) and NVF-P (polysulfone, Sample B), using the aqueous solution of dextran with a broader molecular weight distribution. All the molecular weight cut-off curves plotted as $${SC}_{obs}$$ versus filtration flow rate ( Q F ) exhibited smooth profiles without intersecting each other, showing distinct variations depending on Q F across a wide range of molecular weights. Field emission scanning electron microscopy (FE-SEM) observations revealed that the equivalent pore diameters of samples A and B were nearly identical at 23.0 ± 15.5 nm and 23.3 ± 15.5 nm, respectively. Although the surface porosity of sample A (14.5 ± 3.9%) was higher than that of sample B (10.2 ± 3.2%), the difference was not statistically significant. These numerical data were in excellent agreement with the qualitative morphological findings obtained from the FE-SEM images. Furthermore, it is suggested that the subtle structural differences between the two membranes are also reflected in the relationship between the real sieving coefficients ( $${SC}_{real}$$ ) calculated by using $${SC}_{obs}$$ and the equivalent pore diameters. Since the lab-scale modules are fabricated relatively easily by hand, this methodology is extremely valuable to rigorously define membrane performance.