A Mesopore-Confined and Graphene Oxide-Localized Ruthenium Catalyst Increases Rates of Mid-Chain Polyolefin Hydrogenolysis

High Resolution Image Download MS PowerPoint Slide A catalyst architecture with mesoporous silica coating Ru nanoparticles on reduced graphene oxide (mSiO 2 /Ru/rGO) localizes the 2 nm Ru solely at the closed bottoms of 2.9 nm diameter mesopores. mSiO 2 /Ru/rGO catalyzes the rapid, selective hydrogenolysis of polyolefins at wax formation rates (ν wax ) up to 1700 g wax ·g Ru –1 ·h –1 and a turnover frequency (TOF) for C–C bond cleavage of 130 ± 8 min –1 . The ν wax and TOF for mSiO 2 /Ru/rGO are 23× and 16× those of nonporous Ru/rGO, respectively, indicating that faster chain cleavage is also more selective inside mesopores. The methane yield from mSiO 2 /Ru/rGO is ca. 30% of the value obtained from Ru/rGO. Methane decreases, and wax selectivity improves with narrow-pore (2.3 nm) mSiO 2 /Ru/rGO. The reaction rate decreases at lower and higher H 2 pressures from its maximum at 37 bar. Log(TOF)-log( P H2 ) plots reveal rates ∝ [ P H2 ] 2.8 or [ P H2 ] −2.0 in the lower or higher pressure ranges, respectively. Corresponding plots for Ru/C give rates ∝ [ P H2 ] 1 or [ P H2 ] −2.4 . Ru is hydrocarbon-covered at low pressure; thus, the higher H 2 order for mSiO 2 /Ru/rGO indicates that mesopores increase the density of cleavable unsaturated moieties on the Ru surface. The lower H 2 order on Ru/C implies a lower density of cleavable groups because saturated segments occupy a larger fraction of the Ru surface. Higher surface occupancy by the hydrocarbon reactant correlates with more methane formation. Therefore, pore confinement, narrower pore diameter in mSiO 2 /Ru/rGO, or higher H 2 pressure leads to lower methane yields. Ru nanoparticles in mSiO 2 /Ru/rGO maintain equivalent activity and selectivity over five recycling tests.