Comparative Study of Hostile Environments on the Impact Behavior of Laminated Composites

Glass fiber reinforced epoxy laminates (GFRP) are increasingly used in structural applications where combined mechanical and environmental loading is unavoidable, such as in the aerospace, naval, automotive, and petrochemical industries. This study investigates the influence of aggressive environments on the impact response and damage mechanisms of GFRP laminates. Specimens were immersed in acidic (hydrochloric and sulphuric) and alkaline solutions (sodium hydroxide), oil (automotive engine and automotive brake fluid), and cementitious solutions (cement and metakaolin mortars) for a determined period to simulate severe service conditions. Low-velocity impact tests were subsequently performed to evaluate the residual impact performance in terms of absorbed energy, maximum force, and damage extent. The results demonstrate that environmental exposure significantly alters impact behavior, mainly through matrix plasticization, fiber-matrix interface degradation, and microcrack development. For shorter immersion times (12–30 days), the solutions are not highly aggressive, as the decrease in elastic energy remains below 15%, with cementitious solutions showing the lowest reductions even for longer exposure periods. In contrast, longer immersion times in alkaline solution, DOT4 oil, and metakaolin mortar lead to more severe deterioration, with elastic energy reductions between 30% and 40%, the most aggressive condition being immersion in NaOH for 36 days, which caused a 37.4% decrease. Alkaline and automotive brake fluid oil environments induced the most severe degradation, leading to reduced impact resistance and increased damage propagation.