Dual Beam Laser Welding of Superduplex Stainless Steel: Microstructure, Mechanical Properties, and Electrochemical Behavior

Dual beam laser welding of UNS S32750 superduplex stainless steel was performed to investigate the effect of beam-power distribution on microstructure and mechanical properties. Plates with a thickness of 3 mm were welded at a constant total power and travel speed using leading and lagging power splits of 50:50, 80:20, and 65:35. The heat affected zone width was metallographically estimated at approximately 100 µm for all conditions, consistent with comparable gross thermal exposure under constant nominal linear energy input (Ptotal/v). A slight modification to the power distribution altered the solidification texture and austenite morphology. The 50:50 configuration produced a refined ferritic matrix with a continuous network of grain boundaries, Widmanstätten, and intragranular acicular austenite. The 80:20 condition increased ferrite path continuity, while the 65:35 split produced an intermediate morphology. Vickers hardness reached a maximum for the 80:20 split (HAZ: 345 HV; weld metal: 349 HV). Ultimate tensile strength remained statistically constant between 908 MPa and 914 MPa, whereas elongation decreased from 28% at 50:50 to 24% at 80:20 and 23% at 65:35. All welds exhibited ductile fracture with microvoid coalescence, and electrochemical performance was comparable, with critical pitting temperature values between 78 °C and 91 °C. Beam power distribution primarily affects solidification morphology and enables control of the hardness-to-ductility balance, with a 50:50 split providing the most favorable combination of properties.