Pilot-Scale Investigation of Bauxite Tailings Dewatering by Decanter Centrifuge—Part 1: Process Performance and Fine Particle Recovery

The management of fine bauxite tailings, rich in clay minerals, represents an environmental and operational challenge for the aluminum industry. This study (Part 1) presents a pilot-scale investigation into the dewatering of these ultrafine tailings using a decanter centrifuge, 0.62 m in diameter, as an alternative to conventional wet storage. Tests were conducted at three bowl speeds, 1600 rpm, 1700 rpm, and 1800 rpm, corresponding to G-forces of 888, 1003, and 1124 G. The feed slurry behaved as a non-Newtonian, yield-pseudoplastic fluid, as confirmed by rheology tests. A comprehensive mass balance and performance analysis were conducted. The results demonstrated a monotonic improvement in key performance metrics with increasing bowl speed. Accordingly, increasing the G-force from 888 G to 1124 G improved the final cake solid content from 66.3% to 71.5% (by weight), together with an increase in the average solid recovery from 40.0% to 56.2%. Partition curve analysis revealed the primary limitation: while recovery of particles coarser than 20 µm was very high (>98%), recovery of particles finer than 20 µm remained low, ranging from 22.0% to 35.1%. Partition curve analysis using the Whiten model identified a mechanical cut size (d50c) ranging from 9.72 µm to 12.0 µm. Hydraulic bypass increased from 8.35% to 14.9% with increasing bowl speed, indicating a significant non-size-selective component of separation. Rheological analysis further showed that the apparent viscosity at 100 s−1 decreased from 0.332 to 0.111 Pa·s across the tested conditions, confirming enhanced slurry mobility and its contribution to increased ultrafine bypass. While overall solid recovery reached 56.2% at 1124 G, the mechanical capture of the ultrafine fraction (<5 µm) remains the primary bottleneck for industrial viability. It is concluded that while the decanter centrifuge is mechanically viable for producing a high-solid cake, the limited recovery of fines would create an unsustainable circulating load in an industrial plant. These results demonstrate that G-force alone, within the tested range, is insufficient to manage these tailings and provide the basis for the mathematical modeling required to design the process, as described in Part 2 of this investigation.