Effect of Nb on Solidification Cracking, Mechanical Properties and Corrosion Resistance of 310S Austenitic Stainless-Steel Welded Joints

In this study, 310S austenitic stainless-steel was welded using a laser with varying amounts of Nb to systematically investigate the effect of Nb on solidification cracking susceptibility, mechanical properties, and corrosion resistance of the weld. Under the present experimental conditions, the critical restraint width was higher for the 0.58 wt.% Nb and 1.45 wt.% Nb welds than for the Nb-free and 2.3 wt.% Nb welds, indicating that Nb addition affected the solidification cracking response of the weld. At low-to-moderate Nb contents, Nb can aggravate compositional segregation and increase the presence of low-melting-point liquid films, thereby increasing cracking susceptibility. At higher Nb contents, the reduced cracking susceptibility was accompanied by microstructural refinement and changes in the distribution of Nb-rich constituents during solidification. With increasing Nb content, the number of precipitated phases in the weld increases, mainly distributed at the austenite grain boundaries in granular, elongated, and chain-like forms. The introduction of Nb generally increases the microhardness and tensile strength of the welded joint, attributed to grain refinement strengthening and solid-solution strengthening. The reduction in area first increased and then decreased, suggesting that excessive Nb addition may reduce ductility because of the increased amount of grain-boundary precipitates and local strengthening heterogeneity. With increasing Nb content, the Ir/Ia ratio decreased from 67.6% to 52.2%, suggesting improved intergranular corrosion resistance. This improvement is likely related to the preferential reaction of Nb with carbon, which may suppress the formation of Cr-depleted zones at grain boundaries. Overall, Nb addition improved the corrosion resistance and increased the hardness and tensile strength of the weld; however, its effect on solidification cracking susceptibility was non-monotonic, indicating that careful control of Nb content is required to balance cracking susceptibility, mechanical properties, and corrosion resistance.

Authors

Institutions

Publication Details

Journal
Metals
Published
2026-05-19
DOI
https://doi.org/10.3390/met16050554
Primary Topic
Hydrogen embrittlement and corrosion behaviors in metals
Type
article
Field-Weighted Citation Impact
0.00
Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Effect of Nb on Solidification Cracking, Mechanical Properties and Corrosion Resistance of 310S Austenitic Stainless-Steel Welded Joints

Xulei Wu, D Q Wang, Yulu Su
Metals
Hydrogen embrittlement and corrosion behaviors in metals
article

Effect of Nb on Solidification Cracking, Mechanical Properties and Corrosion Resistance of 310S Austenitic Stainless-Steel Welded Joints

Xulei Wu, D Q Wang, Yulu Su
article en

Abstract

In this study, 310S austenitic stainless-steel was welded using a laser with varying amounts of Nb to systematically investigate the effect of Nb on solidification cracking susceptibility, mechanical properties, and corrosion resistance of the weld. Under the present experimental conditions, the critical restraint width was higher for the 0.58 wt.% Nb and 1.45 wt.% Nb welds than for the Nb-free and 2.3 wt.% Nb welds, indicating that Nb addition affected the solidification cracking response of the weld. At low-to-moderate Nb contents, Nb can aggravate compositional segregation and increase the presence of low-melting-point liquid films, thereby increasing cracking susceptibility. At higher Nb contents, the reduced cracking susceptibility was accompanied by microstructural refinement and changes in the distribution of Nb-rich constituents during solidification. With increasing Nb content, the number of precipitated phases in the weld increases, mainly distributed at the austenite grain boundaries in granular, elongated, and chain-like forms. The introduction of Nb generally increases the microhardness and tensile strength of the welded joint, attributed to grain refinement strengthening and solid-solution strengthening. The reduction in area first increased and then decreased, suggesting that excessive Nb addition may reduce ductility because of the increased amount of grain-boundary precipitates and local strengthening heterogeneity. With increasing Nb content, the Ir/Ia ratio decreased from 67.6% to 52.2%, suggesting improved intergranular corrosion resistance. This improvement is likely related to the preferential reaction of Nb with carbon, which may suppress the formation of Cr-depleted zones at grain boundaries. Overall, Nb addition improved the corrosion resistance and increased the hardness and tensile strength of the weld; however, its effect on solidification cracking susceptibility was non-monotonic, indicating that careful control of Nb content is required to balance cracking susceptibility, mechanical properties, and corrosion resistance.

MetalsVol. 16(5)
Jiangsu University (CN), Jiangsu University of Science and Technology (CN)
Openalex Percentile: Top 11%
Hydrogen embrittlement and corrosion behaviors in metals
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.