Effect of directed energy deposition process parameter on build quality of tantalum

Tantalum is a refractory metal used in a variety of harsh environment applications. Additive manufacturing of tantalum is limited based on its high melting point and affinity for oxygen. Directed Energy Deposition is an additive manufacturing technique with rapid deposition time and compositional flexibility within builds. Additively manufactured tantalum is susceptible to a variety of material and process-based defects. Various lack-of-fusion defects were identified resulting from excessive powder feed rates or insufficient laser power. Oxygen impurities in some samples caused cracking and increased material hardness. Precipitates were identified in the highly oxidized samples which were printed immediately after the build chamber was opened. High-density, low-defect parts were successfully produced. The effects of scan speed, laser power, and powder feed rate on density and defects were analyzed. A processing window was identified for producing high-quality parts which requires adequately high laser power and lower powder feed rate.