Structural Continuity-Controlled Stress Evolution and Distortion in LPBF Bridge Structures

Unsupported and weakly supported overhang features remain a critical challenge in laser powder bed fusion (LPBF) due to their strong susceptibility to geometric degradation, residual stress accumulation, and part distortion. In this study, bridge-shaped structures with four different arch sizes are fabricated to systematically investigate geometry-dependent macroscopic forming quality, stress evolution, and distortion behavior. Experimental results show that increasing arch size leads to progressive thickness reduction at the arch bottom and eventual overhang closure loss, indicating a monotonic deterioration in geometric fidelity. A thermo-mechanically coupled finite element model is developed and calibrated using 3D scanning measurements of warpage, achieving a maximum deviation below 0.03 mm between predicted and measured displacements. Numerical analyses reveal that larger arch sizes promote local heat accumulation and reduced cooling rates beneath the arch, which reduce the instantaneous load-bearing capacity of the material and increase its susceptibility to downward deformation. Meanwhile, arch size significantly influences the establishment of structural continuity and stress transfer during printing; incomplete closure in large arches interrupts load-bearing paths and alters stress redistribution at intermediate stages, whereas similar stress evolution trends are observed once geometric continuity is achieved. These findings demonstrate that arch closure acts as a key structural transition controlling stress transmission and distortion development during LPBF, thereby providing mechanistic insight into geometry-induced defects and offering quantitative guidance for the design of unsupported features in additively manufactured components.