Corrosion Resistance of Arc Ion-Plated CrN/CrAlN Multilayer Coatings Before and After Wear Testing: Interface Effects in Marine Environments

In marine service environments, material surfaces inevitably suffer from wear damage, which can compromise the integrity of protective coatings and further affect their corrosion resistance. Therefore, investigating the post-wear corrosion resistance of coatings is of great significance. In this work, single-layer CrN coatings, CrAlN coatings, and CrN/CrAlN multilayer coatings were deposited on stainless-steel substrates by arc ion plating, and the microstructure, tribological properties, and corrosion behavior before and after wear were systematically investigated. Wear tests were performed under applied loads of 2.5 N and 5 N. The corrosion behavior in the unworn condition and the post-wear corrosion resistance condition was evaluated in a 3.5 wt.% NaCl solution. The results showed that all coatings exhibited a face-centered cubic (FCC) structure, while the CrN/CrAlN multilayer coating possessed the smallest average grain size (13.47 nm). Under applied loads of 2.5 N and 5 N, the CrN/CrAlN multilayer coating exhibited the lowest wear rate, indicating the best wear resistance. In the unworn condition, the CrN/CrAlN multilayer coating showed the lowest corrosion current density (2.74 × 10−10 A/cm2) and the most positive corrosion potential (0.025 V), demonstrating the best corrosion resistance. After wear under a load of 5 N, the CrN/CrAlN multilayer coating retained a low corrosion current density (3.35 × 10−10 A/cm2), in contrast to the marked increases observed for the single-layer coatings. The enhanced performance is considered to be mainly associated with the periodic heterogeneous interfaces in the multilayer structure, which help suppress crack propagation and prolong the penetration path of corrosive media.