Influence of Combined Waste-Based Materials on Fine-Grained Concrete Properties

This study investigates the influence of waste-based materials, namely drinking water treatment sludge (DWTS) and expanded glass production waste (EGPW), on the properties of fine-grained concrete when used as partial Portland cement replacements. Fine-grained concrete mixtures containing different proportions of DWTS and EGPW were evaluated in terms of hydration behavior, microstructural development, mechanical performance, durability, and dimensional stability. Density, ultrasonic pulse velocity, water absorption, flexural and compressive strengths, drying shrinkage, and porosity parameters were determined, while frost resistance was assessed and predicted based on porosity characteristics. Hydration kinetics were analyzed using X-ray diffraction and semi-adiabatic calorimetry. The results showed that increasing EGPW content enhanced cement hydration processes and promoted matrix densification through pozzolanic reactions, resulting in reduced water absorption and improved mechanical properties. In contrast, DWTS exhibited an inhibiting effect on hydration due to its inert nature and high Fe2O3 content, acting primarily as a micro-filler; however, when combined with EGPW at moderate dosages, DWTS contributed positively to flexural strength and slightly reduced drying shrinkage. The combined use of DWTS and EGPW enabled the formation of a balanced pore structure and improved the durability of fine-grained concrete. Among the tested mixtures, ED-3 (7.5% EGPW + 5% DWTS) provided the most favorable balance between hydration activation and binder reduction, while the highest frost resistance was achieved by the ED-4 mixture, reaching approximately 603 predicted freeze–thaw cycles. Overall, the results indicate that properly optimized combinations of EGPW and DWTS can significantly enhance the performance and durability of fine-grained concrete while controlling drying shrinkage.