Remineralization Effect of a Strontium-Containing Composite: An In Vitro Study

The aim of this in vitro study was to evaluate the ability of the new strontium-containing composite, Stela (SDI, Victoria, Australia), to induce hydroxyapatite formation and promote remineralization of demineralized dentin, compared to SDR Flow+ (York, PA, USA). Twenty-four dentin slices (1 mm thick) were obtained from extracted wisdom teeth using a microtome and demineralized with 17% EDTA for 2 h. A layer of either Stela or SDR Flow+ was applied to each slice, allowed to set, and preserved in 0.1% thymol solution. Samples were analyzed at 1, 7, 14 and 28 days (n = 3 per group and time). Measurements were taken at baseline, after demineralization, and after application. Apatite formation was assessed using Fourier-transform infrared spectroscopy (FTIR), while changes in the Calcium/Phosphate (Ca/P) ratio were evaluated by Energy Dispersive Spectroscopy (EDX). Statistical comparisons were performed using the Wilcoxon test (p < 0.05). Both materials promoted carbonated hydroxyapatite formation and increases in calcium and phosphate. Stela exhibited an apatite peak (1420 cm−1) as early as 24 h and significant increases in calcium and phosphate from day 7. SDR Flow+ reached its peak at 14 days and showed significant increases in the Ca/P ratio. By 28 days, both materials achieved comparable remineralization, confirming their effectiveness in treating demineralized dentine.