Swing-Arc Narrow-Gap Submerged Arc-Welding Process Assisted by Pre-Embedding Cold Wires

-CaO phases. This interlayer strengthens the chemical bonding between slag and weld, thereby impeding slag removal. Microstructure evolution analysis of the multilayer welded joint revealed that the variable-angle design increases the groove volume and, combined with the heat-absorbing effect of the additional wires, accelerates molten pool cooling, thereby refining grains in both the weld metal zone and reheat-affected zone. Meanwhile, the tempering exerted by the heat-affected zone (HAZ) of the subsequent weld layer on the previous layer is attenuated. This promotes the gradual transformation of hard-brittle lath martensite in the coarse-grained heat-affected zone (CGHAZ) of the bottom layer into tougher tempered martensite/bainite in the CGHAZ of the upper layers. As a result, the hardness uniformity within the HAZ, the critical weak region of the joint, was enhanced by 54%, enabling synchronous improvement in microstructural homogeneity, hardness distribution, and overall welding efficiency.