Microstructural Damage Evolution and Interfacial Failure Mechanism of NC-UHPC Composites Under Seawater Wet–Dry Cycling

Composite specimens of normal concrete (NC) and ultra-high performance concrete (UHPC) in marine tidal zones are susceptible to coupled physico-chemical degradation under seawater wet-dry cycling; however, the microscopic damage-evolution mechanisms within the NC/overlay transition zone (OTZ)/UHPC three-phase region remain unclear. In this study, accelerated erosion was conducted using 10-fold concentrated artificial seawater under 0, 30, 60, and 90 wet-dry cycles. The X-ray computed tomography, mercury intrusion porosimetry, backscattered electron imaging coupled with energy dispersive X-ray spectroscopy and slant shear tests were employed to systematically investigate the macroscopic bonding performance and microscopic structural damage of NC-UHPC composites. The results show that the interfacial bond strength initially increases and then declines, exhibiting a 13.53% improvement after 30 wet-dry cycles and a sharp 41.55% decrease after 90 cycles compared with that after 60 cycles. The damage severity was the highest in NC, intermediate in OTZ, and lowest in UHPC. The gas-rich pore region within the OTZ provides a stress-buffering effect during the early stage of corrosion. After 90 wet-dry cycles, the total porosity increased by 0.14%, with external porosity increasing by 0.21% and internal porosity decreasing by 0.07%, indicating a pore-structure reconfiguration characterized by micropore coalescence and an increased proportion of macropores. These findings clarify the damage process associated with seawater erosion, pore expansion, and interfacial failure, providing theoretical support for the repair design and durability assessment of marine concrete structures.