Homogeneously Blending PBAT with Silanized Cellulose for Composite Film: Characterization and Physicochemical Property

-hexyldimethylsilylated cellulose (TDMS-Cell). TDMS-Cell/PBAT composite films were then prepared by solution blending and casting in tetrahydrofuran (THF). Structural characterizations confirmed the successful grafting of TDMS-Cl onto cellulose chains, resulting in TDMS-Cell with a degree of substitution of approximately 2. Microstructural observations combined with thermal analysis revealed that TDMS-Cell exerted a dual effect on the crystallization behavior of PBAT: it acted as a heterogeneous nucleating agent that increased the crystallization temperature, while the pronounced steric hindrance simultaneously suppressed crystal growth. Mechanical testing showed that simultaneous strengthening and toughening were achieved at an optimal TDMS-Cell loading of 3-5 wt%. Specifically, the tensile strength increased from ~16 MPa for neat PBAT to 21 MPa (31.25% improvement), and the elongation at break increased from ~700% to 964% (37.7% improvement). In addition, the incorporation of an appropriate amount of TDMS-Cell effectively enhanced the surface hydrophobicity of the composite films. At higher filler loading, however, solvent evaporation-induced phase separation led to self-aggregation of TDMS-Cell, which in turn deteriorated both the mechanical properties and surface hydrophobicity of the composites. Overall, this work systematically elucidates the structure-property relationships of silanized cellulose/PBAT composites in a homogeneous solution system, providing a rational basis for interfacial design and property optimization of PBAT/biomass-based composite materials. The prepared TDMS-Cell/PBAT composite films with balanced mechanical strength, tunable crystallization behavior, and improved surface hydrophobicity exhibit great potential for practical applications in high-performance flexible packaging materials, functional film substrates, lightweight composite structural components, and tunable hydrophobicity coating substrates.