Surface normal emissivity measurements in uncoated and oxidized B-coated plasma facing component materials in the long wavelength infrared spectrum

• Sigrafine® graphite emissivity did not increase with oxidized boron surface layers. • TZM alloy emissivity increased with oxidized boron surface layers. • TZM alloy and Sigrafine® graphite emissivity did not monotonically increase with temperature. Accurate surface emissivity measurements are integral to the fidelity of the infrared thermography diagnostic evaluation in fusion reactors. The emissivities of ATJ TM graphite, Sigrafine® (R6510) graphite, and TZM alloy were measured as a function of temperature in accordance with the Contact Thermometer Method in the ASTM E1933 standard. Samples were heated resistively in a high-vacuum chamber, and the surface temperature was monitored using a surface thermocouple and a Telops long-wavelength infrared camera. The surfaces of Sigrafine® graphite and TZM alloy samples were coated with 10 nm and 20 nm layers of oxidized boron and were also measured in the uncoated condition. The thickness was assessed from measurement by a quartz crystal microbalance (QCM). ATJ TM graphite was uncoated. The measured emissivity of ATJ TM Graphite ranged from 0.82 to 0.83, uncoated Sigrafine® graphite ranged from 0.76 to 0.98, and uncoated TZM alloy ranged from 0.11 to 0.13. Oxidized boron coatings increased the emissivity of the TZM alloy to 0.18–0.23 but decreased the emissivity of Sigrafine® graphite to 0.56–0.66 for a 10 nm coating and to 0.65–0.74 for a 20 nm coating. In contrast to the expected blackbody radiance, the emissivity of uncoated Sigrafine® graphite and TZM alloy did not monotonically increase with temperature from 100 to 500 ℃.