Solar-Activated Self-Cleaning Calcium Sulfoaluminate Cement Modified with Blast Furnace Slag and TiO2

The development of cementitious materials with multifunctional performance is increasingly important to address environmental demands and durability requirements in modern infrastructure. This study investigates calcium sulfoaluminate (CSA) cement partially substituted with blast furnace slag (BFS), fly ash (FA), and TiO2 nanoparticles, aiming to combine sustainability with photocatalytic self-cleaning functionality. Phase analysis by X-ray diffraction confirmed the formation of characteristic CSA hydration products, including ettringite, ye’elimite, anhydrite, and calcite, indicating that partial substitution did not disrupt the primary hydration mechanisms. Microstructural observations revealed that the incorporation of BFS, FA, and TiO2 induced noticeable morphological changes, with increased porosity and microstructural heterogeneity at higher replacement levels. Mechanical testing showed that moderate BFS contents of 5 to 10 wt% enhanced compressive strength in reference mixtures, while systems containing TiO2 exhibited slightly lower strength values and increased dispersion, particularly at elevated slag contents. The photocatalytic performance, evaluated through Rhodamine B degradation under solar irradiation, demonstrated a marked improvement for TiO2-containing samples, reaching degradation efficiencies of up to 80%, in contrast to negligible activity in unmodified systems. These results confirm that the combined use of industrial by-products and photocatalytic nanoparticles in CSA-based matrices represents a viable strategy for producing sustainable cementitious materials with added environmental functionality, without compromising fundamental structural performance.