Understanding Mechanical Properties of Nothofagus alpina (Poepp. & Endl.) Oerst. Wood Through Controlled Freeze–Heat Treatments: Linking Physical, Chemical, and Structural Changes

Wood is a versatile material; however, it is susceptible to changes when exposed to extreme temperatures. This study investigated the physical, chemical, and mechanical properties of raulí (<i>Nothofagus alpina)</i> under different thermal stress conditions. The results showed that the moisture content at temperatures below 5 °C exhibited a significant reduction from 9.7% to 7.5% within the first 20 days. Conversely, under extreme cold (-20 °C), significant changes only occurred after 60 days, with an increase from 9.7% to 11%. At higher temperatures (50 °C, 95 °C, and 120 °C), moisture content dropped sharply after 40 days, nearing 0%. Additionally, analysis showed minor color changes in samples at low temperatures: RW2 (20 d; 5 °C, ΔE* = 3.46) and RW7 (40 d; 5 °C, ΔE* = 0.61); however, color changes were observed at higher temperatures (95-120 °C). RW15 (60 d; 120 °C, ΔE* = 37.16), indicating the degradation of cell wall polymers. Mechanical testing using three-point bending demonstrated that controlled heat treatments can improve the modulus of elasticity (MOE), modulus of rupture (MOR), and fracture energy. The most significant improvements were obtained at 120 °C for 60 days, with increases in MOE, MOR, and fracture energy of 22%, 60%, and 118%, respectively, compared to untreated wood.