In Situ Fabrication of Metal Matrix Composite Using Solid-State Mechanical Mixing

Friction stir-welding (FSW) is widely recognized as a modern solid-state technology used to join dissimilar materials by solid-state mechanical mixing. Such mechanical mixing can be exploited to fabricate in situ composite structures through solid-state deformation mechanisms. The present investigation highlights the microstructural evolution and mechanical properties of an in situ composite structure fabricated by FSW of aluminum (Al) to titanium (Ti) incorporating a thin Nickel (Ni) interlayer. A 0.1 mm thick Ni foil was placed across the full butt interface between 4 mm thick Al and Ti plates before friction stir-welding. Properties of the composite were investigated in detail, and the results revealed that fragmented Ti and Ni particles of different sizes were consolidated in the weld nugget. Al, on the other hand, exhibited substantial microstructural refinement and developed an equiaxed microstructure with random grain orientation, mixed grain boundaries and low micro-strain accumulation in the weld nugget. At the processing temperature, Al reacted with both Ti and Ni to form multiple intermetallic compounds. Tensile testing indicated that the tensile properties of the weld were close to those of the base aluminum. This retention of mechanical properties in spite of recrystallization is attributed to the following mechanisms: (1) Ti and Ni undergo severe deformation, forming fine particles with varying sizes and shapes; (2) at particle interfaces, diffusion and chemical reactions produce interlayers and intermetallic compounds; (3) these particles are consolidated within dynamically recrystallized Al, imparting composite characteristics to the weld nugget; and (4) the particles containing intermetallic compounds act as dispersoids in the Al matrix. Quantitatively, the weld retained 98% (104.2 ± 3.3 MPa) UTS and 90% (17.1 ± 1.2) ductility of base aluminum, demonstrating the effectiveness of the Ni interlayer approach in controlling brittle intermetallic formation.