Biocidal Activity of Multicomponent Magnetron-Sputtered Glass Coatings Against Pathogenic Fungi and the Chromista Phytophthora infestans

The antimicrobial activity of multicomponent, magnetron-sputtered glass coatings was evaluated against phytopathogenic fungi (Botrytis cinerea, Fusarium oxysporum, Cladosporium fulvum, Alternaria solani) and the chromista Phytophthora infestans, with Aspergillus fumigatus included as a model opportunistic pathogen. Fourteen Cu-based multicomponent coatings were deposited on glass using multi-alloy targets composed of Sn, Zn, Al, Ni, Fe, Ti, Mn, Nb, or Co in two high-transmittance variants (≥85% and ≥88%). Antimicrobial activity was assessed in two assays: (A) spore survival after 24–72 h contact, and (B) hyphal growth over 7 days following coating exposure under light and dark conditions. Spore viability decreased after incubation on high-Cu coatings, which showed inhibition for most strains, particularly B. cinerea, F. oxysporum, and P. infestans. The effects on spore germination were independent of the direct transmittance value of the coated glass. Hyphal growth was generally less affected by a high Cu content for most strains. Hyphal growth of F. oxysporum, C. fulvum, A. solani and B. cinerea was reduced by up to 30% on selected multicomponent coatings. For most strains, hyphal growth showed no inhibition after light incubation on coatings. However, light-dependent effects were observed for A. solani, A. fumigatus and P. infestans, while B. cinerea and C. fulvum showed reduced sensitivity during the first two days. High-Cu coatings were most effective at inhibiting spore germination, whereas hyphal growth on multicomponent coatings may respond to different ions. Therefore, high-Cu, two-component coatings may be recommended for practical greenhouse applications.