Fabrication and Properties of Axially Compressed Isotropic Epoxy-Bonded NdFeB Magnets with Partial Rare-Earth Substitution

This work investigates the fabrication and performance of axially compressed isotropic epoxy-bonded NdFeB-type magnets produced from melt-spun powders with partial substitution of (Nd,Pr) by (La,Ce). Four alloy compositions were synthesized and processed into bonded magnets using two powder-to-binder weight ratios (95:5 and 96.5:3.5). Structural analysis confirms that all substituted alloys retain the tetragonal Nd2Fe14B phase (up to ~95 wt%) even at high substitution levels, while the lattice parameters decrease slightly with increasing (La,Ce) content. Microscopy analysis confirms a homogeneous distribution of the binder phase around the powder particles, demonstrating uniform binder–powder integration. Thermal analysis reveals composition-dependent Curie temperatures and enhanced crystallization onset in highly substituted powders. Magnetic measurements on both powders and bonded magnets show that increasing substitution leads to a gradual reduction in remanence, coercivity, and energy product, though all samples maintain strong hard-magnetic behavior. Increasing the powder fraction to 96.5 wt.% significantly improves all magnetic parameters due to higher magnetic-phase density and enhanced interparticle coupling, yielding bonded magnets with densities up to ~80% of the theoretical value. The resulting magnets achieve competitive performance, uniform field distribution and isotropic magnetization with (BH)max values about 65 kJ/m3, a coercivity around 660 kA/m, and superior thermal stability compared with commercial bonded NdFeB magnets. Overall, partial substitution with light rare-earth elements (La,Ce) provides a cost-effective route to high-density bonded NdFeB magnets that combine strong magnetic performance, enhanced thermal stability, and suitability for lightweight, complex-shaped industrial applications. Surprisingly, the coefficients of the temperature variation of coercivity and (BH)max are much better compared to the commercial NdFeB bonded magnets.