Effect of Rapid Solidification on the Structure and Properties of Ag–Cu–(Ti,Zr) Brazing Alloys for Metal–Ceramic Joining

Four compositions of rapidly quenched ribbon brazing alloys based on Ag–Cu–Ti (Ag–26.5Cu–1.5Ti, Ag–25Cu–5Ti) and Ag–Cu–Zr (Ag–26.5Cu–1.5Zr, Ag–25Cu–5Zr) systems were produced. Initial ingots were synthesized by arc melting. Rapidly solidified ribbons, 50–100 μm thick, were then fabricated from homogenized ingots using a “Crystall-702” facility. A comparative analysis of the microstructure and phase composition of both the ingots and ribbons was conducted using scanning electron microscopy and X-ray diffraction. The analysis revealed the presence of Cu4Ti and CuTi intermetallic compounds in the Ag–Cu–Ti alloys, and AgCu4Zr and Zr2Cu in the Ag–Cu–Zr alloys. Rapid quenching was found to produce metastable structures and significantly refine the intermetallic phases. Microhardness measurements of the ingot and ribbon states demonstrated a substantial influence of the processing route on the mechanical properties. The tensile strength of the ingots was also evaluated. The wetting angles of the rapidly quenched alloy melts on 99% Al2O3 (alumina) ceramic substrates under vacuum were determined. All produced ribbons, except for the Ag–26.5Cu–1.5Zr composition, demonstrated adequate wettability. Thus, these materials are considered promising for further research into heat-resistant metal–ceramic joints.