Mechanics of pore array collapse and interaction in shock-compressed polymethyl methacrylate (PMMA)

Recent studies on dynamic pore collapse have revealed significant development of shear localization, which can lead to material failure in porous structures and hot spot generation in energetic materials. These findings have dramatically improved the understanding of failure mechanisms during pore collapse but also prompt further investigation of realistic porous materials. In particular, porous media consist of many pores and porous networks. Even in low-porosity materials, pores can form in close proximity during the manufacturing process, leading to the critical question of pore–pore interaction during collapse under dynamic loading conditions. This study investigates, via plate impact experiments coupled with high-speed internal digital image correlation and shadowgraphy techniques, the collapse of two pores in shock-compressed PMMA at stresses between 0.4 and 1 GPa. The results of these experiments provide new insights into shear localization in pore collapse, in addition to distinct interactions between pores. Shadowgraphy measurements reveal novel, direct visualization of shear band development and crack evolution from pore surfaces. Spacing between adiabatic shear bands is measured over a range of impact stresses and is predicted accurately by the Grady–Kipp model. Pore interactions are found to effect a transition in the impact stress threshold at which different failure mechanisms initiate and are also found to possibly influence preferential sites for shear cracking. Throughout the study, numerical and theoretical models are leveraged to understand shear localization behavior. The role of baroclinicity and wave interactions between the pores is used to elucidate interaction mechanisms between pores.