Influence of Low Zn Concentrations on Behavior of Historical Organ Pipes and Its Model Analogs

This study focused on investigating the influence of zinc on tin pest, both alone and in combination with lead and copper. Based on the known composition of the organ pipe from Trpín, five model alloys were prepared, from which model samples were produced. The model alloys were exposed to low temperatures for 100 days or until complete degradation occurred. The kinetics of the transformation were compared for annealed and non-annealed samples. It was confirmed that the transformation is much faster in samples with retained internal stress. A comparison of the Avrami coefficients indicated similar nucleation behavior for both sample types. Phase transformation was observed in samples containing tin, copper, zinc, and lead, as well as those containing only copper and lead. This suggests that even a relatively small amount of zinc (0.25 wt.%) and copper (0.9 wt.%) can affect the course of tin pest in an alloy containing 13 wt.% lead. Transformation progressed more slowly in samples with only 0.25 wt.% zinc than in pure tin, likely due to the limited solubility of zinc in a tin with low concentrations of alloying elements. The crystallographic structure of both the model alloys and the original historical pipe material was studied using transmission electron microscopy (TEM). In almost all model samples, zinc was uniformly dissolved in the tin matrix. However, in the original pipe, zinc was primarily located at grain boundaries and in association with copper. This indicates that zinc was not intentionally added to the historical alloy but likely appeared in the alloy as a contaminant of impure copper.