Effect of Pre-Conditioning Temperature and Method of Curing on the Shear Bond Strength of Dual-Cure Composite Cements to Dentin

Dual-cure composite cements are an important element of modern dental prosthetics, enabling a stable and long-lasting bond between prosthetic restorations and tooth tissues. Thanks to the combined mechanism of chemical- and light-curing polymerization, they are characterized by high clinical versatility. Despite their wide application, the impact of storage/pre-conditioning temperature on the mechanical properties of dual-cure composite cements remains unclear. The study evaluated the shear bond strength (SBS) of the bond between four dual cements-Bifix Hybrid Abutment (VOCO GmbH, Cuxhaven, Germany), MaxCem Elite (Kerr Corporation, Orange, CA, USA), EnaCem HF (Micerium, Avegno, Italy), and Multilink Automix (Ivoclar Vivadent, Schaan, Lichtenstein)-and dentin depending on their storage temperature (25 °C or 50 °C) and curing method. The tests were carried out on extracted human permanent teeth. The cements were divided into two temperature groups-stored for 7 days at 25 °C or stored for 7 days at 50 °C-and then each of these two temperature groups was divided into two groups-light- and chemically cured (dual-cured, LC) and chemically cured only (CC). Dual-cured cements showed higher shear bond strength at 25 °C. Storage at 50 °C lowered the SBS values, especially for the purely chemically bound cements. LC Bifix Hybrid Abutment achieved the highest SBS at 25 °C, but at 50 °C its properties deteriorated. EnaCem HF showed higher strength at a lower temperature; MaxCem Elite was stable at both temperatures, whereas Multilink Automix showed lower SBS at 50 °C. The study showed that the chemical composition of cements, especially the presence of a benzoyl peroxide (BPO) initiating system, can play a key role in their SBS when bonded to teeth tissue and stability at different storage temperatures. MaxCem Elite showed the best resistance to temperature changes-it achieved the highest temperature stability in both temperature groups.