Radiative Defects in Chloride-Activated CdSe Thin Films

Defect recombination limits wide-gap Se-based chalcogenide devices, yet how chloride activation reshapes radiative pathways remains unclear. Here we show that a 40 min CdCl₂ anneal converts evaporated CdSe from porous nanograins into dense micrometer-scale polycrystals and sharpens the optical band edge, reducing the Urbach energy from 85 to 17 meV at 300 K. Combining temperature- and fluence-dependent photoluminescence (PL), time-resolved PL, hyperspectral mapping, and hybrid-DFT, we resolve three emissive channels and identify their mechanisms. The near-edge band is excitonic at low temperature and evolves into free-carrier emission at elevated temperature. A sub-gap band at <i>E</i> _<i>g</i> -0.45 eV requires above-gap carriers and thermally quenches with a 0.16 eV activation energy. A broad ∼1.05 eV infrared band is excited by above- and below-gap photons and retains microsecond lifetimes at room temperature; patial mapping links it to edge-rich microstructure. Calculations suggest selenium-vacancy and cadmium-vacancy-chlorine complexes, pointing to routes to suppress defect-related losses in wide-gap chalcogenide devices.