Corrosion Properties and Performance of Nanostructured Multilayered Chromium–Amorphous Carbon Coatings on HS6-5-2 Steel

Magnetron-sputtered coatings consisting of multiple alternating layers of chromium and amorphous carbon (Cr/a-C)ml were deposited on HS6-5-2 steel with an intermediate chromium layer by varying deposition rates. Three series of coatings, S1, S2, and S3, with thicknesses of 1.74, 1.15, and 1.14 μm and average chromium contents of 89.3, 66.0, and 59.7 wt.% Cr, respectively, were obtained. Open-circuit potential, cyclic potentiodynamic measurements, and electrochemical impedance spectroscopy were used to characterize their corrosion resistance in 3.5% NaCl. The surfaces were observed with optical and scanning electron microscopy before and after the corrosion tests, and changes in the elemental composition were monitored by energy-dispersive spectroscopy. The protective properties of coatings from series S2 and S3 are similar and significantly better than those of S1. They are characterized by a corrosion current below 1 μA cm–2 and a stable passive state up to over 0.9 VAg/AgCl. The coatings have cathodic behavior towards the substrate, and when the coatings are damaged, galvanic corrosion causes deep pits. Coatings deposited at lower rates and with higher carbon content demonstrate significantly enhanced corrosion resistance in 3.5% NaCl. All three series of Cr/(Cr/a-C)ml@HS6-5-2 exhibit identical corrosion behavior after compromising the coatings’ integrity.