Kinetic Energy Evolution in the Impact Crushing of Typical Quasi-Brittle Materials

Crushing is a critical step in the efficient utilization of quasi-brittle materials such as ores and solid wastes. During this process, materials undergo fracture, and the product particles are ejected, carrying significant kinetic energy. This study investigates typical quasi-brittle materials—concrete and quartz glass—by conducting impact crushing tests using a drop-weight apparatus under varying contact modes and input energy levels. High-speed camera was employed to capture the fracture patterns of the materials and the trajectories of the ejected particles, enabling the calculation of kinetic energy during crushing. The results indicate that under point contact loading, both kinetic energy and its proportion increase significantly with rising input energy. In contrast, under surface contact loading, the kinetic energy and its proportion exhibit minimal change as input energy increases. The average ejection velocity of particles from quartz glass specimens during crushing was 6.28 m/s, which is 2.21 times that of concrete specimens. Moreover, the average proportion of kinetic energy in quartz glass crushing was 5.049%, approximately 14.43 times greater than that in concrete. Enhancing material toughness and adopting surface contact loading help reduce both the kinetic energy and its proportion during crushing. This research contributes to minimizing kinetic energy loss and improving the efficiency of energy utilization in crushing processes.