Hybrid Fe3O4-Gd2O3 Nanoparticles Prepared by High-Energy Ball Milling for Dual-Contrast Agent Applications

This work investigates the feasibility of synthesis hybrid x Gd₂O₃ + (100 - x) Fe₃O₄ nanoparticles using the scalable method of high-energy ball milling for dual-contrast magnetic resonance imaging applications. Comprehensive studies of the structure, magnetic and functional properties of the hybrid nanoparticles were conducted. It was found that the milling process initiates the transformation of the cubic phase c-Gd₂O₃ (Ia3¯) into the monoclinic m-Gd₂O₃ (C2/m). Measurements of the magnetic properties showed that the specific saturation magnetization of the Fe₃O₄ phase is substantially reduced, which is a characteristic feature of nanoparticles due to phenomena such as surface spin disorder and spin-canting effects. The transmission electron microscopy results confirm the formation of hybrid Fe₃O₄-Gd₂O₃ nanostructures and the measured particle sizes show good correlation with the X-ray diffraction results. A comprehensive structure-property relationship study revealed that the obtained hybrid nanoparticles exhibit high r₂ values, reaching 160 mM^-1s^-1 and low r₁ values, a characteristic that is determined primarily by the presence of a large fraction of Gd₂O₃ particles with sizes of ≈30 nm and Fe₃O₄ crystallites of ≈10 nm.