Surfactant-Modified Acidic Magadiites as Adsorbents for Enhanced Removal of Eosin Y Dyes: Influence of Operational Parameters

Organophilic acidic magadiites were prepared after an acidic magadiite (A-Mgd) reaction with cetyltrimethylammonium solutions containing different anions, such as cetyltrimethylammonium bromide (C16TMABr), cetyltrimethylammonium chloride (C16TMACl), and cetyltrimethylammonium hydroxide (C16TMAOH). The resulting materials were studied as adsorbents for Eosin Y removal from artificially contaminated solution. Successful preparation of oganophilic A-Mgd was achieved using C16TMAOH solution with an increased basal spacing from 1.21 nm to 3.15 nm and uptake C16TMA amount of 1.16 mmol/g. Meanwhile, no variation in the basal spacing of 1.20 nm occurred using C16TMACl and C16TMA Br solutions with an uptake mount of 0.07 to 0.09 mmol/g, respectively. Other techniques supported the behavior of the counteranion of surfactant solution on the synthesis of organophilic A-Mgd samples. 13C CP/MAS NMR data revealed that C16TMA cations displayed all-trans conformation comparable to C16TMABr solid, and 29Si MAS NMR confirmed the stability of the host silicate layers during the reaction. The specific surface area of A-Mgd was reduced after the intercalation of C16TMA cations from 38 m2/g to 11 m2/g. The removal properties of organophilic samples were investigated under different conditions, including the Eosin Y pH solution, initial concentration, dosage mass, and content of C16TMA cations. The maximum removal amount was 70 mg/g at acidic pH and using A-Mgd prepared from C16TMAOH solution, while the other organophilic A-Mgds exhibited low removal amounts of 3 to 5 mg/g. The regeneration tests indicated that the efficiency was maintained after four reuse tests with a drop of 30 to 50% from the initial value after seven cycles. The adsorber batch design was employed to estimate theoretically the required masses of used samples to treat an effluent volume of 10 L at a removal percentage of 95% at a fixed initial concentration of 200 mg/L. In total, 20 g of organophilic prepared from A-Mgd and C16TMAOH solution was needed, while 243 g of sample prepared from C16TMABr solution was required. This study proposes the development of a cost-effective, sustainable solution for dye-contaminated wastewater treatment.