Effect of Peel Ply-Induced Surface Roughness and Wettability on the Adhesive Bonding of GFRP Composites

Adhesive joint failure remains a critical limitation in the manufacturing of large wind turbine blades, where reliable and reproducible surface preparation methods are required at an industrial scale. This study systematically evaluates the effect of peel ply-induced surface morphology and chemistry on the adhesion performance of glass fiber-reinforced polymer (GFRP) laminates, explicitly examining the relationship between wettability and bonding strength. Five surface conditions were generated during vacuum-assisted resin infusion using different commercial and proprietary peel plies and a smooth mold surface. Despite significant differences in contact angle and surface energy, lap shear testing revealed no significant relationship between wettability and joint strength. Instead, surface roughness-driven mechanical interlocking and adhesive–substrate compatibility dominated performance. Compared to the smooth mold surface, twill-type peel ply–modified adherends increased shear strength by up to 3.9×, while other commercial types of peel-plies presented strength improvements between 2.7 and 3.3×. More compatible adhesive–polymer resin systems exhibited a combination of cohesive and adhesive failures, with no clear dependence on surface roughness. In contrast, when the adhesive is less compatible with the substrate, surface roughness significantly affects the adhesive response, with adhesive failure predominating. The adhesive application temperature showed no measurable effect for practical industrial use. These findings demonstrate that wettability alone is not a reliable predictor of adhesion performance for this class of substrates and confirm peel ply surface modification as a robust, scalable solution for industrial wind blade bonding.