The Modulated Hot Spot Formation of Void Defects During Laser Initiation in RDX Energetic Crystals

The interaction between laser irradiation and energetic materials is critically influenced by microstructural void defects that determine local energy deposition and initiation sensitivity. In this work, a three-dimensional finite-difference time-domain (3D-FDTD) method was employed to investigate the modulation effects of void defects on optical field distributions and hot spot formation in RDX energetic crystals. The influences of void geometry, spatial position, and void number on the modulation of the incident laser beam were systematically analyzed. It reveals that void defects exhibit strong focusing and scattering behavior, leading to localized high-intensity regions both inside RDX bulk crystals and in void defects. For a single void defect, increasing either the width or depth can significantly enhance the peak electric field and thus the laser sensitivity of RDX crystals. When two voids are present, the number of high-intensity spots first increases and then decreases with increasing separation distance, and the strongest modulation effects are obtained at separations of 0.75λ–3λ. Furthermore, as the number of void defects increases, the modulation effect intensifies, promoting the formation of more hot spots. These findings provide quantitative insight into how void structures govern laser–matter interactions in energetic crystals, offering guidance for understanding and controlling laser initiation behavior.