The Influence of Graphene Oxide Concentration and Sintering Atmosphere on the Density, Microstructure, and Hardness of Al2O3 Ceramics Obtained by the FFF Method

Highly filled (78 wt.%) alumina filaments with various (0.05, 0.10, 0.25 vol.%) graphene oxide concentration for Fused Filament Fabrication (FFF) were obtained. In order to evaluate the effect of graphene oxide on density, microstructure, and hardness, the fabricated materials were sintered in an argon atmosphere at 1500 °C and 1550 °C. A sample that was sintered under the same conditions in air was used as a control. Raman spectroscopy confirmed the reduction in graphene oxide and the absence of carbon in samples sintered in argon and air, respectively. In addition, in the samples with graphene oxide, the alumina grain size was lower than in air-sintered samples. The composite with the lowest amount (0.05 vol.%) of graphene oxide showed the highest value (1670.73 ± 136.9 HV) hardness.