Highly Printable Fe3Al Intermetallic Alloy

Intermetallic Fe3Al-based alloys reinforced with Laves-phase precipitates are emerging as potential replacements for conventional high-alloy steels and possibly polycrystalline Ni-based superalloys in structural applications up to 700 °C. Their impressive mechanical properties, however, are offset by limited fabricability and poor machinability due to their severe brittleness. High tool wear during finish-machining, which is still required for components such as turbine blades, remains a key barrier to their broader adoption. In contrast to conventional manufacturing routes, additive manufacturing offers a viable solution by enabling near-net-shape manufacturing of difficult-to-machine iron aluminides. In the present study, laser powder bed fusion was used to produce an Fe-25Al-1.5Ta intermetallic containing strengthening Laves-phase precipitates, and the porosity, microstructure and phase composition were characterized as a function of the process parameters. The results showed that preheating the build plate to 650 °C effectively suppressed delamination and macrocrack formation, even though noticeable cracking still occurred at the high scan speed of 1000 mm/s. X-ray tomography revealed that samples fabricated with a lower scan speed (500 mm/s) and a higher layer thickness (0.1 mm) contained larger, irregularly shaped pores, whereas specimens printed at the same volumetric energy density (40 J/mm3) but with different parameter sets exhibited smaller fractions of predominantly spherical pores. All samples contained mostly elongated grains that were either oriented close to <001> relative to the build direction or largely texture-free. X-ray diffraction confirmed the presence of Fe3Al and C14-type (Fe, Al)2Ta Laves phase in all samples. Hardness values fell within a narrow range (378–398 HV10), with only a slight reduction in the specimen exhibiting higher porosity.