Tribological and Low Temperature Behavior of ZTA Composites with Graphene Oxide Addition Reinforced with Ductile Particles

The objective of this research was to assess the tribological performance and the capacity to withstand low-temperature degradation of alumina-zirconia-tantalum (ZTA) ceramic-metal composites, modified with 0.5 vol.% graphene oxide (GO) under ball (alumina) on disk dry sliding conditions. The studied ceramic and ceramic-metal composites reinforced with 20 vol.% of tantalum particles were prepared using a colloidal mixing and sintered at a temperature of 1500 °C using a spark plasma sintering technique. In contrast to ZTA ceramic, the wear performance of composites with metal particles and graphene oxide was significantly improved, regardless of the chosen load (10 N and 40 N). The results showed an improvement in the friction coefficient of about 20% and 15% at low and high load, respectively. The wear rate was reduced by 2 and 7 times at 10 N and 40 N, respectively. Raman and energy dispersive spectroscopy confirmed that ZTA-Ta-rGO composites exhibited superior wear resistance primarily because a protective tribolayer formed on their surfaces during wear. This layer effectively lubricated the surfaces, leading to a decrease in both friction and the rate of material loss. Furthermore, these composites exhibited excellent resistance to low-temperature degradation. The results obtained will serve as a starting point for future biomedical testing directions, opening up new perspectives for the use of these materials in biomedicine.