Mechanistic Insights Into Fatigue Life Enhancement of High‐Strength Steel via Ultrasonic Impact Treatment

ABSTRACT This study explores the impact of Ultrasonic Impact Treatment (UIT) on the fatigue performance of high‐strength microalloyed steel commonly used in crankshaft applications. Building on prior observations of fatigue life improvement with UIT, this work focuses on unraveling the process–structure–performance relationships underpinning these enhancements. Microstructural analysis revealed significant grain refinement in the near‐surface layers, with deformation depth increasing at higher impact energies. This led to increased surface hardness and the development of deeper compressive residual stresses, particularly in samples treated with higher impact energy. Rotating bending fatigue testing showed a substantial improvement in fatigue life for UIT‐treated samples, with the endurance limit nearly doubling compared with untreated specimens. Fractographic analysis revealed a transition in crack initiation from surface defects in untreated samples to interior regions in UIT‐treated samples, characterized by the formation of noninclusion‐induced granular bright facets (GBFs). The observed fatigue enhancement is attributed to the synergistic effects of strain hardening and compressive residual stresses, which increase the surface crack threshold and promote interior crack initiation. This study provides new mechanistic insight into UIT‐induced fatigue resistance and interior failure behavior in high‐strength steels.