Reduced hysteresis in La_0.7Ce_0.3Fe_11.5Si_1.5 hydrides by grain size reduction

Magnetic cooling technology, based on the magnetocaloric effect (MCE), offers an energy-efficient and eco-friendly alternative to conventional gas compression, but is often hindered by large magnetic hysteresis, which limits cyclic performance. In this study, we show that the hysteresis of La_0.7Ce_0.3(Fe,Si)₁₃ hydrides – a promising material for room-temperature refrigeration – can be significantly reduced by refining the microstructure of the precursor alloy. Substituting Ce for La in (La_0.7Ce_0.3)(Fe,Si)₁₃H_x increases hysteresis losses from 12.3 J/kg to 34 J/kg. However, preparing the precursor alloy using the melt-spinning technique can almost eliminate this hysteresis. Lorentz transmission electron microscopy (Lorentz-TEM) shows that phase transition nucleation preferentially occurs at the grain boundaries. The hydrides prepared from melt-spun ribbons exhibit a much larger volume fraction of grain boundaries due to finer grains, providing a higher density of nucleation sites. This reduces the energy barrier for the phase transition and weakens the magneto-structural phase transition, as confirmed by <i>in-situ</i> X-ray diffraction patterns. Consequently, the reduced phase transition energy barrier leads to significantly lower hysteresis in melt-spun hydrides samples. These findings demonstrate the potential of microstructure engineering to reduce hysteresis in (La,Ce)(Fe,Si)₁₃Hₓ materials for room-temperature magnetocaloric applications. Microstructure refinement via melt-spinning significantly reduces hysteresis in La_0.7Ce_0.3(FeSi)₁₃ hydrides by reduction of energy barrier for phase transition, enhancing magnetocaloric performance for room-temperature applications.