Effect of artificial aging on fracture toughness and hardness of 3D-printed and milled 3Y-TZP zirconia.

Purpose This study aimed to evaluate the impact of artificial aging on the fracture toughness and hardness of three-dimensional (3D)-printed and computer-aided design and computer-aided manufacturing (CAD-CAM) milled 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP).Materials And Methods Forty bar-shaped specimens (45 × 4 × 3 mm) were prepared using two manufacturing technologies: 3D printing (LithaCon 3Y 210, Lithoz GmbH, Vienna, Austria; n = 20) and milling (Initial Zirconia ST, GC, Japan; n = 20) of 3Y-TZP. The chevron-notch beam method was used to assess the fracture toughness according to ISO 24370. Specimens from each 3Y-TZP group were divided into two subgroups (n = 10) based on the artificial aging process (autoclaving): nonaged and aged. Nonaged specimens were stored at room temperature, while aged specimens underwent autoclave aging at 134°C under 2 bar-pressure for 5 h. Subsequently, the specimens were immersed in absolute 99% ethanol using an ultrasonic cleaner for 5 min. Each specimen was preloaded by subjecting it to a 4-point loading test, with a force of up to 200 N applied for three cycles. Further 4-point loading was conducted at a rate of 0.5 mm/min under controlled temperature and humidity conditions until fracture occurred. The maximum force (F) was recorded and the chevron notch was examined at 30 × magnification under an optical microscope for measurements before the fracture toughness (K) was calculated. Microhardness testing was also performed to measure the Vickers hardness number (VHN). A scanning electron microscope (SEM) coupled with an energy dispersive X-ray unit (EDX) was used to examine surface topography and chemical composition. X-ray diffraction (XRD) was conducted to identify crystalline structure. Data were statistically analyzed using two-way ANOVA and Student's t-test with a significance level of 0.05.Results The nonaged 3D-printed 3Y-TZP group exhibited a significantly higher fracture toughness value (6.07 MPa m) than the milled 3Y-TZP groups (p < 0.001). After autoclave aging, the 3D-printed 3Y-TZP group maintained significantly higher fracture toughness (p < 0.001) compared to the milled 3Y-TZP group. However, no significant differences in hardness values (p = 0.096) were observed between the aged and nonaged groups within each manufacturing process (3D-printed and milled) independently.Conclusion The findings revealed that the new 3D-printed 3Y-TZP produced by the lithography-based ceramic manufacturing (LCM) technology exhibited superior fracture toughness after autoclave aging compared to the milled 3Y-TZP. While no significant differences in hardness were observed between the aged groups, the 3D-printed material demonstrated greater resistance to fracture, indicating enhanced mechanical stability.