Enhanced Proton Conduction in Metal–OrganicFrameworks through Single-Crystal to Single-Crystal Transformation

In this work, an anionic framework Co-MOF (<b>1</b>) was elaborately constructed, which underwent single-crystal-to-single-crystal (SC-SC) transformation to produce <b>1-Cr</b> and <b>1-Fe</b> after immersion in a CrCl₃ or FeCl₃ solution. Despite the similar crystal structure, the significantly enhanced proton conductivities of <b>1-Cr</b> and <b>1-Fe</b> far exceed that of <b>1</b> at all humidity and temperature conditions. Even at 30 °C and 98% RH, the proton conductivity of <b>1-Cr</b> and <b>1-Fe</b> can reach up to high values of 1.49 × 10^–2 and 6.39 × 10^–3 S cm^–1, respectively, surpassing that of <b>1</b> by over 5000 times under identical conditions. The partial alteration of the proton-conducting carriers from metal-water cluster [Co­(H₂O)₆]·6H₂O] (<b>1</b>) to metal-hydroxyl-water clusters [Cr­(OH)₄(H₂O)₂]·6H₂O] (<b>1-Cr</b>) and [Fe­(OH)₄(H₂O)₂]·6H₂O] (<b>1-Fe</b>) can be attributed for the above-mentioned enhanced performance. The introduction of hydroxyl by SC-SC transformation can establish interconnected proton conduction pathways within the proton channels, which greatly facilitate proton conduction, affording much lower activation energies (0.12 eV for <b>1-Cr</b>, 0.18 eV for <b>1-Fe</b>, and 0.28 eV for <b>1</b>). This research demonstrated that SC-SC transformation not only achieved significantly improved proton conduction but also contributed to a deeper understanding of the structure–property relationships, providing new insights into the design of advanced materials with enhanced proton conductivity.