Synthesis, MolecularStructure, and Water ElectrolysisPerformance of TiO₂‑Supported Raney-IrO_<i>x</i> Nanoparticles for the Acidic Oxygen Evolution Reaction

Developing low-cost, highly active, and stable catalysts for the acidic oxygen evolution reaction (OER) at the proton exchange membrane (PEM) water electrolyzer anodes remains a scientific priority. Reducing the iridium loading while increasing the intrinsic activity of the catalysts is essential for cost-effective hydrogen production. Here, we address a family of TiO₂-supported Raney-IrO_<i>x</i> catalysts with low iridium loading and high activity in single-cell PEM water electrolyzer anode environments. A controlled Raney-type Ni leaching process of pristine, supported IrNi alloy phases forms crystalline IrO_<i>x</i> nanoparticles (NPs) featuring metallic Ir-rich cores surrounded by more amorphous IrO_<i>x</i> surfaces. This structure is shown to be conducive to catalytic activity and the suppression of membrane poisoning due to Ni degradation. The trace amounts of Ni remaining after leaching in the IrO_<i>x</i> NPs result in heterogeneous crystal structure and induce local lattice strain. Further, we synthetically strike a balance between conductivity and activity and succeed to narrow down the notorious large performance gap between liquid electrolyte rotating disk electrodes (RDEs) and single-cell membrane electrode assembly (MEA) electrolyzer measurements. OER stability numbers (<i>S</i>-numbers) of the identified Raney-IrO_<i>x</i> anode catalysts surpass commercial IrO₂ catalysts, confirming the stability of these catalysts. The PEM electrolyzer tests reveal that Raney-IrO_<i>x</i> anodes achieve 3 A cm^–2 at 1.8 V with a low geometric Ir loading of ca. 0.3 mg_Ir cm^–2, meeting the technically important power specific Ir utilization target of 0.05 g_Ir/kW.