High-PerformanceEnergy Storage in Ba(Al_0.5Nb_0.5)O₃‑Modified (Bi_0.5Na_0.5)TiO₃‑Based Lead-Free Ceramics via High-EntropyStrategy

Lead-free dielectric capacitors are widely utilized in high-power pulse devices due to their outstanding power density, rapid charging–discharging speed, and environmental friendliness. However, there are still challenges in further improving their energy storage performance. Recently, a high-entropy strategy has received widespread attention to obtain high-performance dielectric capacitors. In this work, Ba(Al_0.5Nb_0.5)O₃ (BAN) was introduced into lead-free (Bi_0.5Na_0.5)TiO₃-based ceramics to increase configuration entropy and chemical disorder, exploiting a synergistic high-entropy strategy to optimize the energy storage characteristics. Remarkably, superior energy storage density (<i>W</i>_rec ∼7.40 J/cm³) and efficiency (η ∼85.5%) at a great electric breakdown strength (<i>E</i>_b ∼547 kV/cm) are achieved in 0.85(0.6(Bi_0.5Na_0.5)TiO₃–0.4(Sr_0.7Bi_0.2)TiO₃)–0.15BAN high-entropy ceramic. The integration of BAN boosts the increase of entropy and induces grain refinement, strengthened relaxation behavior, formation of polar nanoregions, and a widened band gap, leading to reduced <i>P</i>_r and improved <i>E</i>_b as well as excellent energy storage performance. Moreover, good thermal stability, frequency stability, and charge–discharge performance are also realized. This study confirms that high-entropy engineering is a feasible route to realize high-performance energy storage, providing prospective lead-free dielectric materials for practical applications.