Incident excitation effects on ZnO-based photoluminescence

Zinc oxide (ZnO) is an attractive semiconductor material owing to a wide band gap, large exciton binding energy, and strong luminescent properties. Two distinct spectral regions are present in the room temperature emission of this material: a narrow line in the UV/near-UV region that is excitonic in nature and a lower energy broad emission band centered in the green/yellow region. Commercially available ZnO particles containing excess Zn and oxygen vacancy defect sites (referred to as ZnO:Zn) were excited using three light sources to study different radiative recombination regimes of the as-received powders. First, a UV LED at a center wavelength of 365 nm provided low irradiance (0.02-0.08 W/cm²) with varying pulse widths (continuous operation to 16 ns). Second, the third harmonic of a pulsed Nd:YAG laser provided high irradiances (∼10⁴-10⁶ W/cm²) at a fixed nominal pulse width of 5 ns. Finally, a continuous polychromatic synchrotron X-ray source was also used to excite the ZnO:Zn powders. During UV LED excitation, a low number of carriers are created in the material, leading to an anticipated linear relationship between luminescence and irradiance. This held true for defect luminescence; however, there was an observed enhancement of exciton emission relative to the UV LED intensity as the pulse width was decreased, independent of irradiance. During UV laser excitation, the number of carriers was significantly increased, raising the material into a bimolecular recombination regime, which produced exciton emission much stronger than visible band emission. Finally, spectra obtained during synchrotron X-ray excitation, whose continuous illumination and higher penetration depth yielded higher emission from defect sites relative to exciton emission. A redshift in the exciton emission was also observed as excitation pulse width and sample temperature were varied, and is discussed.