Manipulation of Emergent Collective Excitations via Composition Control in Mixed MPX ₃ Correlated 2D Antiferromagnets

Transition metal (i.e., Mn, Fe, Cr) and chalcogen (Se) substituents are introduced into single-crystalline NiPS₃, and the evolution of the two emergent quasi-particle excitations characteristic to the XXZ correlated antiferromagnetism of NiPS₃ (i.e., spin orbit entangled exciton (SOX) and two-magnon scattering (2M )) are investigated as functions of substituent concentration through comprehensive room- and low-temperature photoluminescence (PL) and Raman spectroscopy studies. These findings are further correlated with the magnetic properties of the same set of compounds reported in prior studies. The work revealed that the SOX emission intensities and linewidths are mainly controlled by the magnetic anisotropy and spin orientations, and are strongly suppressed by the introduction of substituents. The suppression depends on the type of substituent, with Fe affecting the SOX emission more than Mn and Cr. The 2 m scattering is linked to short-range correlations and exhibits greater resiliency against metal atom substitution. While the 2M peak at low temperature gets suppressed and red-shifted in frequency with increasing concentrations of all the substituents, Fe induces the weakest suppression compared to all other substituents. Altogether, these findings revealed the introduction of substituents as a powerful route to control the emergent collective excitations in NiPS₃ and mixed-MPX₃ materials.