Effect of Ultrasonic Treatment of Dispersed Carbon Nanocomposite Media on the Formation, Electrical Conductivity, and Degradation of a Hydrogel for Metallic Stimulation Electrodes

This study investigates the impact of ultrasonic treatment on the deagglomeration of aggregates of single-walled carbon nanotubes (SWCNTs) and reduced graphene oxide (rGO). The aim of the research is to enhance the electrical conductivity of a biopolymer hydrogel designed for coating metallic neurostimulation electrodes. Biocompatible coating materials are essential for the safe long-term function of implants within the body, enabling the transmission of nerve impulses to external devices for signal conversion and neurostimulation. Dynamic light scattering (DLS) was employed to monitor the dispersion state, in conjunction with measurements of specific electrical conductivity. The mass loss and swelling capacity were evaluated over an 80-day period to account for the effects of degradation during in vitro studies. Samples of flexible-elastic hydrogels for electrodes with complex geometry were formed by the photopolymerization of a photopolymerizable medium, similar to a photoresist. Analysis of the dependence of temperature and normalized optical transmittance on the duration of laser photopolymerization made it possible to determine the optimal polymerization temperature for the photopolymerizable medium as -28 °C. This temperature regime ensures maximum reproducibility of hydrogel formation and eliminates the presence of unpolymerized areas. The article presents a biopolymer hydrogel with SWCNTs and rGO nanoparticles in a 1:1 ratio. It was found that sufficient specific electrical conductivity is achieved using SWCNTs with a characteristic hydrodynamic radius of R = 490 nm and rGO with R = 210 nm (sample Col/BSA/CS/Eosin Y/SWCNTs (490 nm)/rGO <b>4</b>). The photopolymerized hydrogel <b>4</b> demonstrated sufficient biocompatibility, exceeding the control sample by 16%. According to the results of in vitro studies over 80 days, this sample exhibited moderate degradation of 45% while retaining its swelling ability. The swelling degree decreased by 50% compared to the initial value of 170%. The presented hydrogel 4 is a promising coating material for implantable metallic neurostimulation electrodes, enhancing their stability in the physiological environment.