Hot hydrogen exposure of UxZr1-xCy nuclear fuel: The effect of additional carbon

Nuclear thermal propulsion (NTP) using hydrogen as propellant in a solid-state fission reactor to reach temperatures of up to 3000 K can achieve significantly higher specific impulse than chemical propulsion. A promising fuel that is again considered for NTP is U x Zr 1-x C y . To reduce the overall mass loss as well as the uranium fuel loss, a range of experiments using additional carbon in hot hydrogen (2600 K, 6 SLPM flow rate) were performed for up to 5–6 h. Both a CH 4 addition (0.1 and 0.2 vol%) in the hydrogen stream and the use of sacrificial graphite pieces upstream of the samples were tested, with sample compositions from 5 at% UC to 30 at% UC. The results showed a strong reduction of mass loss, up to a factor of 3, as well as a reduction of surface uranium losses in the presence of additional carbon in the atmosphere. Even with additional carbon in the atmosphere, material with 30 at% UC was not stable, but material with 20 at% UC was stable for up to 6 h. The sample surfaces showed texturing after processing, possibly by grain growth on the surface. This led to a separation into grains with high uranium content close to the (100)-orientation, and with low uranium content in grains close to the (111)-orientation.