Shock compression of additively manufactured high solids loaded polymer composites with aligned porosity

The effects of aligned porosity on the shock-compression response of additively manufactured (AM) composite structures with collinear and log-cabin geometries are investigated. The composites contain two inorganic and two organic particle populations and a UV-curable polymer binder. X-ray phase contrast imaging (X-PCI) is used as an in-material diagnostic in plate-impact experiments performed at the Dynamic Compression Sector of the Advanced Photon Source at the Argonne National Laboratory. Macroscale shock and particle velocities and microscale pore collapse velocities are measured from X-PCI images obtained from samples impacted in various orientations relative to the AM build directions. The linear shock and particle velocity relation for the structures with collinear build geometry shows directional differences, with the build direction exhibiting the highest slope and the filament print direction having the shallowest slope. Composites with log-cabin geometry, due to their slightly lower porosity and smaller sized pores, show higher shock velocities than the collinear structures at the same particle velocity. Microscale directionality effects are also observed, with the pore collapse velocity dependent on the pore configuration. Specifically, the pore collapse velocity is highest for pores elongated along the impact direction which is the case for the colinear structures impacted in the filament print direction, which is consistent with the directionality trend observed in the data for the shock and particle velocity equation of state. The pore collapse velocity approaches ∼80 % of the shock velocity and is several times the average bulk particle velocity, suggesting a highly hydrodynamic mechanism of pore collapse. Overall, both the macroscale response as measured by the shock and particle velocity relationship, and the microscale response as measured by the pore collapse velocity, are found to be anisotropic and dependent on the AM composite structure. • X-ray phase contrast imaging is used to analyze evolution and collapse of pores in the interior of additively manufactured particulate-polymer composites with colinear and log-cabin structures under shock loading. • Microscale observation is correlated with macroscopic shock response measured by the shock velocity-particle velocity relation. • Pore directionality and alignment are found to influence both microscale pore collapse behavior and macroscopic shock response, with lower porosity and smaller pore sizes corresponding to higher shock velocities. • Pore collapse velocity is several times higher than particle velocity, suggesting highly hydrodynamic nature of pore collapse.