Two Times Faster Glycolysis of Poly(ethylene terephthalate) with CaO Filler-Catalyst

Poly(ethylene terephthalate) (PET) is a widely used polymer that accumulates in the environment due to its low degradability, requiring efficient recycling strategies. In this study, CaO filler derived from calcium carbide slag (CS) waste was used for the first time as a catalyst for PET depolymerization. PET/CaO composites were prepared via hot extrusion of PET with the finely dispersed CaO filler. The resulting composite demonstrated consistently higher PET conversion (≥95%) and the yields of dimethyl and dibutyl terephthalates (80 and 84%, respectively). Kinetic studies of glycolysis demonstrated that embedding 1 wt% of CaO in the PET matrix doubled the bis(2-hydroxyethyl) terephthalate (BHET) formation rate relative to an externally added CaO catalyst, which resulted in BHET yields of 84.7% and 41.1% after 40 min. SEM and EDX investigations demonstrated good adhesion between the polymer matrix and the filler. The recovered BHET was successfully re-polymerized to produce recycled PET (r-PET). The maximum rate of weight loss of r-PET samples (at Tmax = 438.7–444.7 °C) was comparable to the original materials (at Tmax = 455.3–457.7 °C). In fact, the direct incorporation of CaO catalyst derived from waste into the polymer matrix during additive manufacturing enabled the implementation of an efficient and scalable closed-loop recycling strategy.