Research into the Properties of Wear-Resistant Coatings Produced Using HVOF Technology on the Functional Surfaces of Injection Molds

The paper presents the results of research aimed at verifying the possibility of creating renovation layers using HVOF (High Velocity Oxygen Fuel) technology. HVOF ceramic coatings represent a promising way to increase the efficiency, reliability, and sustainability of manufacturing processes. Molds for high-pressure injection of aluminum alloys were analyzed. The degradation mechanism of the functional surfaces of the molds was determined. The paper analyzes two types of HVOF coatings—Cr2O3-TiO2 and Al2O3-TiO2. For both coatings, a Ni-Al interlayer was used for mechanical stability, durability, and reliable functionality in demanding operating conditions. The interlayer is used in thermal spraying as a so-called bond coat—a layer that mediates adhesion between the metal substrate and the ceramic coating. EDX maps of chemical elements from the coating surface and cross-sections were determined. The tribological properties of the coatings were evaluated by a ball-on-disk test at 20 °C and 250 °C. SEM analysis of the surface after the tribological test was performed. The resistance of the coatings was evaluated by COF and friction resistance.