Evaluation of Sasa kurilensis Biomass-Derived Hard Carbon as a Promising Anode Material for Sodium-Ion Batteries

The depletion of global lithium reserves, coupled with the necessity for environmentally sustainable and economically accessible energy storage systems, has driven the development of sodium-ion batteries (SIBs) as a promising alternative to lithium-ion technologies. Among various anode materials for SIBs, hard carbon exhibits obvious advantages and significant commercial potential owing to its high energy density, low operating potential, and stable capacity retention during prolonged cycling. Biomass represents the most attractive source of non-graphitizable carbon from a practical standpoint, being readily available, renewable, and low-cost. However, the complex internal structure of biomass precursors creates significant challenges for precise control of microstructure and properties of the resulting hard carbon materials, requiring further research and optimization of synthesis methodologies. This work reports the synthesis of hard carbon from Sasa kurilensis via pyrolysis at 900 °C and investigates the effect of alkaline pretreatment on the structural and electrochemical characteristics of the anode material for SIBs. Sasa kurilensis is employed for the first time as a source for non-graphitizable carbon synthesis, whose unique natural vascular structure forms optimal hierarchical porosity for sodium-ion intercalation upon thermal treatment. The materials were characterized by X-ray diffraction, infrared and Raman spectroscopy, scanning electron microscopy, X-ray microtomography and low-temperature nitrogen adsorption–desorption. Electrochemical properties were evaluated by galvanostatic cycling in the potential range of 0.02–2 V at a current density of 25 mAhg−1 in half-cells with sodium metal counter electrodes. The unmodified sample demonstrated a discharge capacity of 160 mAhg−1 by the 6th cycle, with an initial capacity of 77 mAhg−1. The alkaline-treated material exhibited lower discharge capacity (114 mAhg−1) and initial Coulombic efficiency (40%) due to increased specific surface area, leading to excessive electrolyte decomposition.